説明
Military Grade, Fluid Resistant at High Temperature, Heat Shrinkable Identification Sleeves
Thermoplastic cable markers
説明
MSVLO series is military grade cable and wire identification sleeves, which is designed to meet the requirements of outstanding oil resistance. It is made of cross-linked environmentally friendly polyolefin bombarded by high power electron beam with electronic accelerators to meet high end markets where highly reliable cable& wire identification is required. MSVLO conforms to Classes 1 そして 3 of AMS-DTL-23053/6, half-hard high molecular materials. Shrink ratios, both 2:1 そして 3:1 are available. See below tables. MSVLO boasts amazingly high fluid resistance at high temperature for long time like JP-8 used for aviation fuel oil. It is widely used in aviation and spaceships, high speed rails EMU, submarine as well as other military and architecture industries.
特徴
² Fluid resistance at 70°C/158°F for 168h, such as JP-8 fuel oil, temperature rating 135°C /275°F
² High temperature resistant, rated temperature, 135°C
² Highly flame retardant, VW-1
² ROHS compliant
² High reliability, permanent identification
² Heat sensitive, swift recovery
² Computer-printable, any characters and logo are easy to design
Rated Temperature
Continuous operating temperature: -55°C~135°C /-67°F~275°F
分. shrink temperature: 85°C /+185°F
Full recovery temperature: 115°C~200°C /239°F~392°F, 8~3minutes
マックス. storage and transportation temperature: ≤50°C /122°F
Standards
² Meets AMS-DTL-23053/5, compatibility: UL224
² Color code soundness: SAE-AS 81531 and MIL-STD-202F/215J
Dimensions(2:1)
| Order Description | Expanded As Supplied(mm) | Recovered After Heating(mm) | |||
| Inner Diameter ID1 | Flatten width G | Dual Wall Thickness H | Inner DiameterID2 | Single Wall Thickness h | |
| MSVLO-2X-1.6/ | 2.00±0.20 | 3.7±0.3 | 0.48±0.10 | ≤0.79 | 0.45±0.06 |
| MSVLO-2X-2.4/ | 2.79±0.20 | 5.0±0.3 | 0.48±0.10 | ≤1.18 | 0.49±0.06 |
| MSVLO-2X-3.2/ | 3.64±0.23 | 6.3±0.4 | 0.48±0.10 | ≤1.59 | 0.51±0.06 |
| MSVLO-2X-4.8/ | 5.26±0.25 | 8.9±0.4 | 0.49±0.10 | ≤2.36 | 0.54±0.06 |
| MSVLO-2X-6.4/ | 6.92±0.28 | 11.5±0.4 | 0.50±0.10 | ≤3.18 | 0.56±0.06 |
| MSVLO-2X-9.5/ | 10.2±0.32 | 16.7±0.5 | 0.51±0.11 | ≤4.75 | 0.59±0.06 |
| MSVLO-2X-12.7/ | 13.5±0.36 | 21.8±0.6 | 0.52±0.11 | ≤6.35 | 0.60±0.07 |
| MSVLO-2X-19/ | 20.1±0.40 | 32.2±0.6 | 0.53±0.11 | ≤9.53 | 0.62±0.07 |
| MSVLO-2X-25/ | 26.7±0.45 | 42.5±0.7 | 0.55±0.12 | ≤12.7 | 0.63±0.07 |
| MSVLO-2X-38/ | 39.8±0.51 | 63.2±0.8 | 0.57±0.12 | ≤19.1 | 0.64±0.07 |
| MSVLO-2X-51/ | 53.0±0.56 | 83.9±0.9 | 0.58±0.13 | ≤25.4 | 0.64±0.08 |
| MSVLO-2X-76/ | 79.4±0.56 | 125.3±1.0 | 0.59±0.13 | ≤38.1 | 0.64±0.09 |
Dimensions(3:1)
| Order Description | Expanded As Supplied (mm) | Recovered After Heating (mm) | |||
| Internal Diameter ID1 | Flatten Width G | Dual Wall Thickness H | Inner Diameter ID2 | Single Wall Thickness h | |
| MSVLO-3X-1.6/ | 2.00±0.20 | 3.7±0.3 | 0.47±0.10 | ≤0.53 | 0.52±0.06 |
| MSVLO-3X-2.4/ | 2.79±0.20 | 5.0±0.3 | 0.47±0.10 | ≤0.79 | 0.57±0.06 |
| MSVLO-3X-3.2/ | 3.64±0.23 | 6.3±0.4 | 0.48±0.10 | ≤1.06 | 0.61±0.06 |
| MSVLO-3X-4.8/ | 5.26±0.25 | 8.9±0.4 | 0.49±0.10 | ≤1.59 | 0.67±0.06 |
| MSVLO-3X-6.4/ | 6.92±0.28 | 11.5±0.4 | 0.50±0.10 | ≤2.36 | 0.71±0.06 |
| MSVLO-3X-9.5/ | 10.2±0.32 | 16.7±0.5 | 0.52±0.11 | ≤3.18 | 0.77±0.06 |
| MSVLO-3X-12.7/ | 13.5±0.36 | 21.8±0.6 | 0.53±0.11 | ≤4.75 | 0.80±0.07 |
| MSVLO-3X-19/ | 20.1±0.40 | 32.2±0.6 | 0.55±0.11 | ≤6.35 | 0.84±0.07 |
| MSVLO-3X-25/ | 26.7±0.45 | 42.5±0.7 | 0.56±0.12 | ≤8.47 | 0.86±0.07 |
| MSVLO-3X-38/ | 39.8±0.51 | 63.2±0.8 | 0.57±0.12 | ≤12.9 | 0.89±0.07 |
| MSVLO-3X-51/ | 53.0±0.56 | 83.9±0.9 | 0.57±0.13 | ≤17.2 | 0.90±0.08 |
| MSVLO-3X-76/ | 79.4±0.56 | 125.3±1.0 | 0.59±0.13 | ≤25.8 | 0.92±0.09 |
Standard Packaging Data
| No. | Sizes | 包装 (Pcs/Reel) | |
| 箱 210 | 箱 146 | ||
| 1 | Φ1.6 | 2500 | 250 |
| 2 | Φ2.4 | 2500 | 250 |
| 3 | Φ3.2 | 2000 | 250 |
| 4 | Φ4.8 | 2000 | 250 |
| 5 | Φ6.4 | 1500 | 250 |
| 6 | Φ9.5 | 1000 | 250 |
| 7 | Φ12.7 | 500 | 250 |
| 8 | Φ19 | 500 | 250 |
| 9 | Φ25 | 500 | 250 |
| 10 | Φ38 | 250 | 250 |
| 11 | Φ51 | 250 | 250 |
| 12 | Φ76 | 250 | 250 |
Physicochemical& Electrical Performance
| Properties | Indicator | Test Method | ||
| Specific Property | Unit | States | ||
| Tensile Strength | Mpa | Unaged | ≥13.8 | ASTM G 154,MIL-DTL-23053E ISO 37,500mm/min 175°C,168h,ISO 188 |
| Heat aged/After fluid UV aged | ≥11.1 | |||
| Elongation at break | % | Unaged | ≥200 | |
| Heat aged/After fluid | ≥100 | |||
| Secent Modulus | Mpa | Unaged | ≥173 | ASTM D 882 |
| Voltage Withstand | V | Unaged/After aged | 2500V,No breakdown in 60 sec. | IEC 243,ASTM G 154 175°C,168h,ISO 188 |
| Dielectric Strength | MV/m | Before ageing | ≥19.7 | |
| Heat Aged/After fluidUV aged | ≥15.8 | |||
| Volume Resistivity | Ω.cm | Unaged | ≥10 14 | IEC 93 |
| Dielectric Constant | – | Unaged | ≤3.2 | ASTM 150 |
| Water Absorption | – | Unaged | ≤0.5 | ASTM 570,23°C,24h |
| Bare Copper Corrosion | – | Unaged | No corrosion | 23°C,Rh 95±5%,24h 175°C,16h |
| Heat Shock | – | Unaged | No cracks, flowing, dripping | Wind to specified mandrel,225°C,4h |
| Cold Flexibility | – | Unaged | No cracks | Wind to specified mandrel,-30°C,1h |
| Flammability | – | Unaged | VW-1 | IEC 60332-1-3 Ed.1.0 b:2004 |
| Longitudinal Change | % | Unaged | 2X:-10~+1 | 200°C,constant temperature 3min |
| 3X:-15~+5 | ||||
| Smoke Density | – | Unaged | – | DIN 5510-2 |
| Toxicity Index | – | Unaged | – | BS 6853:1999 Appendix B |