1.6mm Aluminium PCB for Lighting Industry

Model NO.
Aluminium PCB-3

Board Thickness
0.8mm,1.0mm,1.2mm,1.6mm,2.0mm,2.2mm

Thermal Conductivity
1.0W/M.K,1.5W/M.K,2.0W/M.K,3.0W/M.K,4.0W/M.K

Ccl Brand
Jh,Ccaf.etc

Sample Date
3-5days

Transport Package
Vacuum Packing

Specification
UL, TS16949, IPC 600 CLASS 2

Trademark
ZAPON

Origin
CHINA

HS Code
85340090

Production Capacity
50000sqm/Month

Description

Aluminum base copper-clad laminate have excellent flame retardant, high mechanical strength, dimensional stability etc. Especially it has very good heat sink, electromagnetic shielding and solder float.

It’s widely used for the modifier and sparker on fire for motorcycle and mobile, power LED, sound box, power supply module and acoustics shielding system etc.

Note: We specially produces Metal Base Copper-Clad Laminates, and our products have been compiled series with all complete specifications.
The tapy and specification of Aluminum based Laminates CCAF-01, CCAF-04-A, CCAF-05etc. And 0.8mm, 1.0mm, 1.5mm, 2.0mm, etc.
Thickness of the copper: 18um, 35um, 70um, 105um.
Base size: 500mm × , 600mm (20″× , 24″); 600mm × , 1060mm (24″× , 42″)

CCAF-04-A Aluminum-base copper-clad laminate
The test base: CCAF-04 the high heat dissipation Aluminum-base copper-clad laminate
Thickness of the copper: 35um
Thickness of the diclectric: 80um(matrial of the high heat dissipation)
Thickness of the aluminum-base: 1.5mm

The result of the test:

  Test item Technology request Unit Test result
1 Peel Strength A ≥ 1.0 N/mm 1.05
After thermal stress (260 ordm;C ) ≥ 1.0 N/mm 1.05
2 Blister test AfterThermal stress (288 ordm;C, 2min) 288ordm;C  2 min
No delaminating		 / OK
3 Themal Resistance ≤ 2.0 ordm;C /W 0.65
4 Flammability(A) FV-O / FV-O
5 Surface Resistivity A ≥ 1 × 10 5 M Ω 5.0 × 10 7
Constant humidity treatment
(90%,3 5 ordm;C ,96h)		 ≥ 1 × 10 5 M Ω 4.5 × 10 6
6
7		 Volume Resistivity A ≥ 1 × 10 6 M Ω@ m 1.0 × 10 8
Constant humidity treatment
(90%,3 5 ordm;C ,96h)		 ≥ 1 × 10 6 M Ω@ m 1.9 × 10 7
8 Dielectric Breakdown (DC ) ≥ 25 Kv/mm 31
9 Dielectric constant (1MHz)
(40 ordm;C, 93% , 96h)		 ≤ 4.4 / 4.2
10 Dielectric dissipation factor (1MHz )
(40ordm;C ,93%,96h)		 ≤ 0.03 / 0.029
  Accelerated aging experiment
(125 ordm;C ,2000h)		   The laminate bace should no wrinkles,no crack,no delaminating or no pine / OK
11 High low temperature impact test
(-50 ordm;C, 15min, 80ordm;C , 15minTOTAL   DO 15 ~ 20 Circulation) 		 Peel Strength / N/mm 1.39 ~ 1.64
Surface Resistivity / M Ω 1.9 × 10 8 ~6.4 × 10 8